Titanium Is Increasing Develop In The Medical Application
Apr 08, 2017

Application of Titanium in Transplantation

 

Artificial joints and artificial bone replacement materials should have the following basic properties: lightweight high-strength materials, with biocompatibility, corrosion resistance, the implant occurred in the body 

reaction does not cause material degradation, repeated stress caused Fatigue, less damage and other properties. The most important properties of metal implants are forming, machine addition and polishing, which must be maintained during the expected life span, without degradation when subjected to fatigue, abrasion, corrosion and impact loads. Titanium and titanium alloys meet all The above requirements. The earliest use of dental powder, polypropylene, plexiglass and other artificial joint materials, low strength, easy to fold, poor biocompatibility. Later, switch to stainless steel, but the proportion of stainless steel larger, about 2 times the proportion of human bones, but also in the body by the role of body fluids will be corrosion and fracture. Co-Cr alloy is also an excellent artificial joint material, but unfortunately, cobalt, chromium elements are toxic to the human body. The titanium and titanium alloy with a small proportion (similar to the proportion of human bone), strength, good mechanical processing, corrosion resistance is excellent, is an ideal artificial joint materials.

 

Surgical use of titanium materials used in the transfer material to pure titanium and Ti-6Al-4VELI alloy-based. Recently, Ti-6Al-7Nb and Ti-13Nb1-13Zr, which have good 

affinity with human body, have also been approved by ASTM standards. With titanium artificial bone, cells can be regenerated on it, bone can grow, titanium and human bone, epithelium, to create tissue has a good affinity. In order to improve the surface quality of the implanted material attached to the human bone, it is also more effective to carry out the bioceramic layer on the roughened surface. At present, titanium and titanium alloy has been widely used in artificial bone joints, artificial bone, joint feet, broken bone fixator, bone marrow, artificial heart valve, skull and so on. According to statistics, China's annual demand for titanium alloy artificial joints more than 5000 sets, the clinical application of good results.

 

Application of titanium in orthopedic surgery

Medical titanium alloy elastic modulus is closer to the human body than stainless steel, suitable for orthopedicsurgery. In orthopedic surgery, the use of titanium-nickel shape memory alloy. The results show that NT-SMA is a new material with anti-wear, corrosion resistance, shape memory effect, pseudo-elasticity and acoustic damping. It is widely used in orthopedics, except for commonly used bone plate, intramedullary nail, mandibular Fixed, scoliosis correction, etc., Shanghai Changhai Hospital NT-SMA and a series of design and clinical applications, such as NT-patellar device, NT-arc fork nails, NT-arc device, NT-spacecraft For the reconstruction of the sacral and design), and achieved satisfactory results.

For the application of titanium alloy materials to the human body, countries are constantly trying to explore, to seek a more secure and reliable new titanium alloy for the benefit of the people around the world.



Titanium in the pharmaceutical industry

Titanium in the pharmaceutical industry is mainly used for the production of containers, reactors and heaters. Pharmaceutical production, equipment often have to contact hydrochloric acid, nitric acid, sulfuric acid and other inorganic acids, organic acids and their salts, equipment due to corrosion is often damaged, and because of steel equipment to bring iron pollution caused by product quality, the use of titanium equipment Can solve these problems. For example, penicillin esterification kettle, saccharification tank, chloramphenicol film evaporator, analgin reactor, Mitel filter, dimethyl sulfate cooler, liquid filter, etc., have a precedent for selection of titanium, The production of the amount of liquid and quality are constantly improving, and the quality of the Chinese Pharmacopoeia in full compliance with the provisions.

 

Application of Titanium in Medical Devices

Titanium and titanium alloy has good corrosion resistance, titanium non-toxic, non-magnetic, is a good choice of medical equipment materials. In the history of the development of surgical instruments, the first generation of surgical instruments made of carbon steel, due to the performance after plating can not meet the clinical requirements were eliminated. The second generation of austenite, ferrite and martensitic stainless steel surgical instruments, but the stainless steel composition of chromium toxicity, off the chrome layer has a certain impact on the human body, therefore, the emergence of the third generation - titanium surgical instruments. Titanium has a light weight characteristic that makes it particularly suitable for microsurgery. Titanium is resistant to corrosion, good elasticity, no deformation, etc., resistant to repeated cleaning, disinfection surface quality is not affected; non-magnetic, can exclude the tiny, sensitive implantation of 

electronic equipment, such as the threat of damage, so that titanium surgical instruments more and more The more widely. Has been used to make surgical blades, hemostats, scissors, electric bone drill, tweezers and so on. In the medical device titanium tube suture needle, sternal suture, one of the heart surgical instruments of the oxygen filter titanium filter, electrocardiogram machine with titanium electrode, in vitro culture machine with titanium makeers; medical ultrasonic crushing Machine probe, blood transport box automatic controller, as well as titanium surgery for ophthalmic surgery, the current use of the situation are good.

Dental Application of Titanium and Titanium Alloys

Titanium has excellent corrosion resistance and human affinity, and consider the metal allergies and specific strength and other suitable for use in the dental field. The metal used in dental surgery, from the twentieth century, twenty years of amalgam and metal crown, etc., the sixties mainly use gold, silver, palladium alloy, after the seventies of stainless steel teeth for permanent and removable equipment The most commonly used materials, nineties titanium casting technology to promote the use of. Dental use titanium casting machine Casting with high dimensional accuracy, no bubbles and shrinkage and other characteristics In the human body for hard tissue repair of metal materials, titanium elastic modulus and human tissue closest, which can reduce the metal implants and bone Organizational mechanical incompatibility. The thermal conductivity of titanium is the lowest of all metal materials for dental restoration, and the low thermal conductivity can reduce the thermal stimulation of dental pulp teeth and is important for dental restoration. Titanium inlay, the crown and so have the protection of pulp, to avoid the role of hot and cold stimulation. Dental titanium in the material, the original mostly titanium, but its strength is insufficient, difficult to grind, there is poor wear resistance, easy to produce casting defects and quality instability and so on. Ti-6Al-4N alloy, but the metal V is harmful to the 

human body, instead of Nb instead of V, the successful Ti-6Al-7Nb alloy has excellent corrosion resistance, and it has excellent corrosion resistance. The human body is basically harmless, but also has a strong plastic, excellent grinding and other advantages, has been made ASTM standards recognized. At present, superelastic Ti-Ni alloy is being used in tooth straightening. From the eighties of the eighties since the developed 

countries began to study the application of titanium in oral repair, first for dental implantation, and later used for denture stent, crown and teeth and teeth, the current titanium can be crown, crown , Fixed bridge, porcelain bridge, adhesive bridge, denture clasp, base, connecting device and stiffening device, almost denture all metal parts can be made of titanium. Titanium and titanium alloys have become a hot spot in dental applications. Titanium alloy porcelain teeth can be a good recovery of the tooth shape and function, and high strength, beautiful appearance, color and stability, smooth surface, wear resistance, corrosion resistance, is a permanent repair body, apply to all fixed teeth, In particular, it is good biocompatibility, sensitive to nickel ions are more suitable, has been widely used in the restoration of teeth.